Ti15333 Sheet

Item: Ti15333 Sheet
Thickness: Above 0.5mm
Width: 50mm-1000
Length: 1500mm
Material: Ti-15V-3Al-3Cr-3Sn
Finish: Polished
Certification: ISO，EN10204 3.1，EN10204 3.2
Standards: ASME SB265, ASTM B265
Shape: Flat, Square, or as the customer requests.

Send Inquiry

Product Introduction

Introduction

Ti-15V-3Cr-3Sn-3Al alloy (TB5) is a β-type titanium alloy, with excellent old rolling and cold forming properties, as well as its welding performance and corrosion resistance. TB5 alloy is mainly used to manufacture sheet metal components and fasteners. It can improve structural and production efficiency, and reduce manufacturing costs as well. The main semi-finished products of the alloy are titanium sheets, titanium strips, and titanium rods, and also produces titanium pipe fittings and castings.

α-β Type Titanium Alloy Properties
Type	Grade	Chemical Composition	Operating Temperature/˚C	Intensity Level/MPa	Application
near β	Ti-15-3	Ti-15V-3Cr-3Sn-3Al	290	≥ 1080	With excellent cold-forming properties, it can form medium and complex sheet metal parts at room temperature. It can also be superplastic in the above 700˚C, and welding performance is excellent. Suitable for making aerospace sheet metal parts and fasteners

Ti-15V-3Cr-3Sn-3Al Alloy Properties
Shape	δ or d/mm	Condition	Room Temperature
Shape	δ or d/mm	Condition	σb/MPa	σP0.2/MPa	δ5/%	δ50/%	ψ/%	α/(.)	τ/Mpa
Sheet, Plate	≤ 3.0	solution treatment	705-945	690-870	≥ 12	-	-	≥ 105	-
		ST+540˚C,8h, air cooling	≥ 1000	≥ 965	≥ 7	-	-	-	-
		ST+520˚C, 8h, air cooling	≥ 1080	≥1010	≥ 6	-	-	-	-
		ST+480˚C,8h, air cooling	≥ 1240	≥1170	≥ 5	-	-	-	-
Rod, Wire	2.5-6.5	solution treatment	705-945	-	-	≥ 15	≥ 60	-	≥ 550
		ST+540˚C, 8h, air cooling	≥ 1000	≥ 965	-	≥ 10	≥ 25	-	≥ 650
		ST+520˚C, 8h, air cooling	≥ 1080	≥ 1010	-	≥ 8	≥ 20	-	≥ 700

Ti-3Al-2.5V Heat Distortion Process Specification
Heat Distortion Type	Heat Temperature/˚C	Final Temperature/˚C	Fire Deformation/%
ingot formation	1000-1050	≥ 850	30-60
billet forging	950-1050	≥ 800	40-60
slap breakdown	1000-1050	≥ 800	40-60
sheet rolling	900-950	≥ 800	40-60
rod rolling	800-900	≥ 750	50-80
rod (wire) rotary swaging	700-740	≥ 600	10-20

Applications

Ti-15V-3Cr-3Sn-3Al titanium alloy is mainly used for high-strength sheet metal parts in aircraft structures and rivets for cold riveting such as aircraft resistance umbrella beams and their matched rivets. In the satellite structure, it is used for distant engine supports and cones. On the civilian field, it is applied in golf heads.

Ti15333 Sheets are mainly used for high-strength sheet metal parts in aircraft structures and rivets for cold riveting. It is also used for aircraft resistance umbrella beams and matching rivets, and in the manufacture of apogee engine supports and support cones of satellite structures.

For civilian applications, it is used to make the hitting surface of the golf club head.

Ti15333 Sheet chemical composition

Ti 15-3-3-3 chemical composition (mass fraction)
Alloy element					Impurities≤
V	Cr	Sn	Al	Ti	Fe	C	N	H	O	Other elements
										Each	Total
14.0-16.0	2.5-3.5	2.5-3.5	2.8-3.6	Balance	0.25	0.05	0.05	0.015	0.13	0.10	0.40

Ti 15-3-3-3 Sheet popular specification

Standard: AMS4914
Thickness (mm)	Width (mm)	Length (mm)
0.8	600	1500
1	1000	2000
1	700	1400
2	500	1500
3	700	1700

Product Description

Standards	ASTM B265, ASME SB265
Product	Ti15333 Titanium Sheets for glass frame
Diameter	≥0.5mm
Width	≤500mm
Length	1000mm-1500mm
Technique	Cold rolling & Hot Rolling
Surface	Bright
Shape	Rectangular/Square/small pieces
Application	eyeglass, glasses frame, etc